The thermal conductivity and mechanical strength of gypsum and gypsum-cellulose plates made from commercial plaster by a new process have been measured. The gypsum parts made by the new process, 'novogesso', have high mechanical strength and low porosity. The gypsum strength derives from both the high aspect ratio of the gypsum crystals and the strong adhesion among them by nano-flat layers of confined water, which behaves as supercooled water. Another contribution to the strength comes from the nano-flatness of the lateral surfaces of the gypsum single crystals. The bending and compression strengths, σB and σc, of gypsum plates prepared by this new technique can be as high as 30 and 100 MPa, respectively. The way gypsum plates have been assembled as well as their low thermal conductivity allowed for the construction of a low-cost experimental house with thermal and acoustic comfort.

Portland cement-based materials are present in our everyday life. Over the last two decades, important developments have been made to improve their mechanical strength, mainly through microstructural design. In addition, another promising parameter still remains in the early stages of understanding: that of adhesion. Recently, interdisciplinary researchers have considered the issue of water confinement by the hydrated cementitious surfaces. It could contribute to increase the adhesion and strength in these materials. On the other hand, ionic and non-ionic chaotropic substances might be able to disorder the structure of such special water. The results presented in this paper show important effects of these chaotropic substances on the strength of cementitious materials. They highlight the role of the confined water on the adhesion, when the microstructural parameters are kept constant. More than contributing to the fundamental understanding of adhesion within cement paste, these results provide basic insights on in-situ nanotechnology.

Expelling of the liquid phase during sintering of ZrO2-6.5 mol% Y2O3- 0.5 mol% Pr2O3 ceramic was observed as a result of grain coarsening. ZrO2- 7.0 mol% Y2O3 samples, without Pr2O3 addition, do not show this effect under the same sintering conditions. The expelling process is caused by surface tension forces and attracting van der Waals forces between the grains, coupled with the existence of two glass phases on the grain boundaries. The amount of expelled glass phase increases with grain growth, but saturates above 16 mm average grain size.